Product description
The main components of hard fire brick are clay and kaolin, and usually a certain proportion of quartz sand, bauxite, coal gangue and other auxiliary raw materials are added. The content of clay is usually between 50% and 70%, and the content of kaolin is between 10% and 30%.
Advantages of hard fire brick
Hard fire brick have good fire resistance: clay firebricks have good high temperature resistance, usually can withstand high temperatures above 1000℃, and some can even reach high temperatures above 1500℃.
Hard fire brick have strong corrosion resistance: clay and kaolin in clay refractory brick materials contain high silicate and aluminate, which can resist various acids, alkali, salt and other chemical corrosion, so it is widely used in chemical industry, metallurgy, electric power and other fields.
Physical and chemical index of hard fire brick
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||
Packages:
Physical and chemical index of hard fire brick
|
Items |
Index |
|
||||||||
|
/ |
N-1 |
N2a |
N2b |
N-3a |
N-3b |
N-4 |
N-5 |
N-6 |
||
|
Refractoriness /℃≥ |
1750 |
1730 |
1730 |
1710 |
1710 |
1690 |
1670 |
1580 |
||
|
0.2Mpa Refractoriness under load(RUL)/℃≥ |
1400 |
1350 |
/ |
1320 |
/ |
1300 |
/ |
/ |
||
|
Reheating linear change/℃(1500℃,2h) |
1400℃,2h |
+0.1 -0.4 |
+0.1 -0.5 |
+0.2 -0.5 |
/ |
/ |
/ |
/ |
/ |
|
|
1350℃,2h |
|
|
|
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
+0.2 -0.5 |
|
||
|
Apparent porosity/% ≤ |
22 |
24 |
26 |
24 |
26 |
24 |
26 |
28 |
||
|
CCS/Mpa ≥ |
30 |
25 |
20 |
15 |
15 |
20 |
15 |
15 |
||